Product

Atlas F

Atlas F has a very good honeycomb structure and special chemical properties, which can be effectively used in all standard industries and processing industries, such as hand lay-up, vacuum infusion, RTM and other processes. It is a globally applicable material, widely used in fields such as wind turbine cabin covers, ships and non-structural parts.

可供厚度:

产品规格

产品特点 / Features

■ Excellent fatigue resistance                                                        


■ Suitable for dynamic load structure                                 


■ Higher resistance to styrene                    


■ Higher temperature resistance                                                                               


■ Resin injection is more ideal                                              


■ Less resin consumption than other foams               


■ Recyclable     

                                                                                                                                     

典型心梗 Typical Performance单位 UnitF50 F60F65F80F100

密度区间

Density Range

ASTM-D1622Kg/m³45-5557-6562-7272-8888-108
压缩强度

Compressive Strength

ASTM-D1621MPa0.400.551.23.87.0

压缩模量

Compressive Modulus

ASTM-D1621MPa2030354570

拉伸强度

Tensile Strength

ASTM-D1623MPa0.400.550.800.801.10

拉伸模量

Tensile Modulus

ASTM-D1623MPa2235405070

剪切强度

Shear Strength

ASTM C273MPa0.350.480.600.600.75

剪切模量

Shear Modulus

ASTM C273MPa5.07.510.012.015.0
剪切伸长率

Shear Elongation

ASTM C273%2525252015
吸水率

Water Absorption

ISO 2896%2221.51.5

初始热导率

Initial Thermal Conductivity

ASTM C518mW/mK2424242525

热变形温度

Heat Distortion Temperature

DIN- 53424100110110120120

使用温度

Service Temperature

/-180,+95-180,+195-180,+195-180,+105-180,+105

阻燃性

Fire Behaviour

DIN 4102-1ClassB3B3B3B3B3